Stellite 12 Hard Facing Welding Rod Weartech WT-12 Green Color Cutter And Blade Outlet Valve Sealing Surface
Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Name | Stellite 12 Hard Facing Rod | Color | Green |
---|---|---|---|
Material | C Si Mn Mo Cr W Ni Fe Co | Welding Current | International Standard |
Test Report | Mill-certificate | Certificate | ISO 9001 |
Diameter | 2.5-8.0mm | Hardness | HRC 44-50 |
Length | 350mm 500mm 1000mm 2000mm 3000mm 4000mm | Process | PTA / Laser Cladding / HVOF / Plasma Spray/ 3D Printing |
Equivalent | Stellite 12, BISHILITE (MHA) No.12, Weartech WT-12, Stoodite 12, POLYSTEL 12 | Application | Pre-protection Of Plastics, Paper-making, Chemical Fiber, Cutter High-pressure Valve Etc |
Melting Range | 1200-1365 ºC | Density | 8.53 G/cm3 |
High Light | Stellite 12 hard facing welding rod,350mm hard facing welding rod,500mm Stellite 12 |
Stellite 12 Weartech WT-12 Stellite 12 Green Hard Facing Rod Green Color Cutter And Blade Outlet Valve Sealing Surface
Product Description
WL-Co12 could be considered an intermediate alloy between WL-Co6 and WL-Co1. It contains a higher fraction of hard, brittle carbides than WL-Co6, and has increased resistance to lowangle erosion, abrasion, and severe sliding wear whilst retaining reasonable impact and cavitation resistance. WL-Co12 is often used self-mated or running against WL-Co6 or WL-Co1. The higher tungsten content provides better hightemperature properties compared to WL-Co6, and it can be used at temperatures up to about 700˚C.
WL-Co12 is typically used for cutting tools that need to withstand abrasion, heat and corrosion. Examples include industrial knives for cutting carpets, plastics, paper and synthetic fibres; and saw tips in the timber industry. It is also used for control plates in the beverage industry, pump vanes, bearing bushes and narrowneck glass mold plungers; and for hardfacing of engine valves, pinch rollers in the metal-processing industries, and rotor blade edges.
Common Names: Stellite 12, BISHILITE (MHA) No.12, Weartech WT-12, Stoodite 12, POLYSTEL 12
Standard: AWS 5.21-2001 ERCoCr-B
Chemical Composition(%)
C |
Si |
Mn |
Mo |
Cr |
W |
Ni |
Fe |
Co |
1.4 |
1.30 |
≤1.00 |
≤1.00 |
30.00 |
8.5 |
≤3.00. |
≤3.00 |
Rest |
Characterisitic
AWS / ASME: A5.21 / SFA5.21 ERCoCr-B |
|
Metal to metal Wear |
Excellent |
Cold / Hot Abrasion |
Excellent/Excellent |
Erosion / Corrosion |
Excellent/Excellent |
Deposit Layers |
2 Max |
Impact |
Good |
Magnetic |
No |
Thermal Conductivity |
14.6 W/m.K, 100 Btu-in/hr/ft2/°F |
Electrical Resistivity |
98 µ-ohm.cm, 38.6 µ-ohm.cm |
Packing Details
For length 350mm 500mm pack in carton each 5kg
For 1000mm packing in 5kg tube, 4 tubes in one 20kg carton
For length more than 1000mm, pack in wooden box directly
Applications
Used for pre-protection of plastics, paper-making, chemical fiber, cutter and blade Outlet valve sealing surface
High temperature and high-pressure valve
Type We Could Offer
Trademark | Nominal Chemical Composition | HRC | Application | |||||||||
C | Cr | Si | W | Ni | Fe | Mn | Mo | Co | B | |||
WL Co1 | 2.45 | 30.0 | 1.0 | 13.0 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 50-58 | Valve seat insets, bearing, sawteeth, rotary ring, Pump Sleeves | |
WL Co3 | 2.4 | 30.5 | 1.0 | 13.0 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 50-56 | Valve seat insets,steel mill guide roll, wearing panel of cracker blade, etc. | |
WL Co4 | 1.0 | 31.0 | 1.0 | 14.0 | ≤3.0 | ≤1.0 | ≤0.5 | ≤0.5 | Bal. | 45-50 | Hot extrusion die, dry battery industry | |
WL Co6 | 1.2 | 29.0 | 1.0 | 4.5 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 40-46 | Engine valve, high temperature valve, turbine blade | |
WL Co12 | 1.4 | 30.0 | 1.3 | 8.5 | ≤3.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 44-50 | Pressure valves, sawteeth screw fights | |
WL Co20 | 2.5 | 32.0 | 1.0 | 17.0 | ≤3.0 | ≤3.0 | ≤0.5 | ≤1.0 | Bal. | 54-59 | Wear plate, bearing sleeve, etc. | |
WL Co21 | 0.2 | 27.0 | 1.0 | 0.2 | ≤3.0 | ≤2 | ≤1.0 | ≤5.5 | Bal. | 20-40 | Fluid valve seat, turbine blades, hot forging die | |
WL Co25 | 0.05 | 20.0 | 1.0 | 15.0 | 10.0 | ≤2.0 | ≤1.5 | ≤1.0 | Bal. | 24 | High temperature and corrosion-resistant valve sealing surface, pressure casting dies, etc. | |
WL Co31 | 0.5 | 26.0 | 1.0 | 7.5 | 10.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 30-35 | Extrusion die, steam turbine blade, etc. | |
WL Co32 | 1.8 | 26.0 | 1.2 | 12.0 | 22.0 | ≤1.5 | ≤0.5 | ≤1.0 | Bal. | 40-45 | Engine inlet and exhaust valve | |
WL Co190 | 3.2 | 26.0 | 1.0 | 14.0 | ≤1.0 | ≤3.0 | ≤1.0 | ≤1.0 | Bal. | 54-60 | Petroleum drill bit, mining industry | |
WL CoT400 | 0.08 | 8.5 | 2.6 | 1.5 | ≤1.5 | ≤1.0 | 28 | Bal. | 0.8 | 50-60 | Valve and roller path, plastic extruder in strongly corrosive | |
WL CoT800 | 0.08 | 18.0 | 3.4 | ≤1.5 | 1.5 | ≤1.0 | 28 | Bal. | 0.8 | 52-58 | Valve and roller path, plastic extruder in strongly corrosive |